Tissue Reactions to Calcium Silicate
Subcutaneous Connective Tissue Reactions to New Calcium Silicate Cements: An Animal Study
The aim of this study was to determine the subcutaneous connective tissue reactions to these new materials.
Materials and Methods These materials were placed in polyethylene tubes and implanted into the dorsal connective tissue of Sprague Dawley rats. The presence of inflammation, edema, necrosis, dystrophic calcification, and thickness of fibrous capsule formation was recorded by histological examination 7, 30, and 60 days after the implantation procedure. Inflammation scores were defined as follows: 0 = no or few inflammatory cells, no reaction, 1 = <25 cells, mild reaction; 2 = 25 to 125 cells, moderate reaction; and 3 = ≥125 cells, severe reaction. Fibrous capsule thickness, necrosis, and formation of calcification were recorded.
Studieöversikt
Status
Betingelser
Intervention / Behandling
Detaljerad beskrivning
24 Twenty-four male Sprague Dawley rats weighing 250--300 gr were used in the study. For preliminary study, 1 one rat was used on each experimental day . During the study period, the animals were kept in cages in groups of five and taken to daily care under standard care conditions without restriction ofno feed and water supply restrictions.
ProRoot White MTA, Medcem Pure Portland Cement, and Medcem MTA mixed according to the manufacturer's' instructions were filled placed into sterile p olyethylene tubules (internal diameter: 1.3 mm internal diameter, x external diameter: 1.6 mm external diameter, x length: 5.0 mm length) sterilized with ethylene oxide gas, as specified by ISO , with using a sterile Llentulo. Twenty-one empty polyethylene tubes remained empty to bewere used as in the control group.
Surgical Procedures The rats were anesthetized in an ether jar, followed byand then received intraperitoneal administration of 70- mg/kg ketamine and 10- mg/kg xylazine intraperitoneally. The operation area (backs) of the anesthetizedeach rats were was shaved with a certain razor blade, and the surgical area was disinfected with Betadine skin disinfectant ,. After shaving, the operation area wasand covered with sterile drapes to be exposed. In orderTo induce local hemostasis, operations of 0.5 cc, 0.006- mg/ml 4% articaine containing epinephrine (Ultracaine D-S-Aventis Forte, Istanbul, Turkey) by infiltrating local anesthesia was performedadministered.
Incision lines were determined marked on the dorsal, anterior, and posterior extremities of the experimental animals, two in the anterior and two in the posterior region and two in the posterior region. When determining the incision lines, cCare was taken to keep a distance of at least 2 cm distance between the placed materials to prevent them from being affected . Skin iIncisions of approximately 1 cm length long was performedwere made with the a sterile scalpel in the designated areas. The cCanals were entered through the incision site with a sterile periosteal elevator, and ducts were opened under the skin by blunt dissection approximately 2 cm deep. Subsequently, polyethylene tubules filled with the experimental material according toof the each groups and sterile empty polyethylene tubules for the control groups were placed in the prepared subcutaneous canals. The incision sites were then closed primarily using 3/0 silk sutures. Antibacterial spray was applied on the sutures.
Histological Procedures After surgery, on the 7th, 30th and 60th days, 7seven animals from each group, (21 animals) were euthanized intraperitoneally with high doses of thiopentalsodium (Pental, İ.E. Ulagay Med. San. , Istanbul, Turkey) administered intraperitoneally under ether anesthesia on Days 7, 30, and 60. Then, tThe test tubules placed were then removed together with the surrounding tissues and placed in bottles containing 10% neutral formalin. Paraffin blocks were prepared from test samples fixed in bottles containing 10% formalin for 2 two days. From the tissues embedded in the paraffin blocks, 4- μm serial sections parallel to the long axis of the tube were taken cut with a microtome (Leica SM 2000R, Leica Instruments, Wetzlar, Germany) and stained with hematoxylin and eosin (H&E).
All histological evaluations were performed The tissue samples were histologically examined under an optical microscope (Nikon Eclipse E 600, Nikon Corp., Tokyo, Japan) at 40×x, 100×x, 200×x, and 400×x magnifications. All the slides were examined and rated by a pathologists blinded to all procedures.
Studietyp
Inskrivning (Faktisk)
Kontakter och platser
Studieorter
-
-
-
Eskişehir, Kalkon, 26040
- Eskisehir Osmangazi University
-
-
Deltagandekriterier
Urvalskriterier
Åldrar som är berättigade till studier
- Barn
- Vuxen
- Äldre vuxen
Tar emot friska volontärer
Testmetod
Studera befolkning
Beskrivning
Inclusion Criteria:
- Male Sprague Dawley rats weighing 250--300 gr
Exclusion Criteria:
-
Studieplan
Hur är studien utformad?
Designdetaljer
Kohorter och interventioner
Grupp / Kohort |
Intervention / Behandling |
---|---|
Control
Twenty-one empty polyethylene tubes remained empty to bewere used as in the control group.
|
The presence of inflammation, edema, necrosis, dystrophic calcification, and thickness of fibrous capsule formation was recorded by histological examination 7, 30, and 60 days after the implantation procedure of materials.
|
ProRoot MTA
ProRoot White MTA mixed according to the manufacturer's' instructions were filled placed into sterile p olyethylene tubules (internal diameter: 1.3 mm internal diameter, x external diameter: 1.6 mm external diameter, x length: 5.0 mm length) sterilized with ethylene oxide gas, as specified by ISO , with using a sterile Llentulo.
|
The presence of inflammation, edema, necrosis, dystrophic calcification, and thickness of fibrous capsule formation was recorded by histological examination 7, 30, and 60 days after the implantation procedure of materials.
|
Medcem MTA
Medcem MTA mixed according to the manufacturer's' instructions were filled placed into sterile p olyethylene tubules (internal diameter: 1.3 mm internal diameter, x external diameter: 1.6 mm external diameter, x length: 5.0 mm length) sterilized with ethylene oxide gas, as specified by ISO , with using a sterile Llentulo.
|
The presence of inflammation, edema, necrosis, dystrophic calcification, and thickness of fibrous capsule formation was recorded by histological examination 7, 30, and 60 days after the implantation procedure of materials.
|
Medcem Pure Portland Cement
Medcem Pure Portland Cement mixed according to the manufacturer's' instructions were filled placed into sterile p olyethylene tubules (internal diameter: 1.3 mm internal diameter, x external diameter: 1.6 mm external diameter, x length: 5.0 mm length) sterilized with ethylene oxide gas, as specified by ISO , with using a sterile Llentulo.
|
The presence of inflammation, edema, necrosis, dystrophic calcification, and thickness of fibrous capsule formation was recorded by histological examination 7, 30, and 60 days after the implantation procedure of materials.
|
Vad mäter studien?
Primära resultatmått
Resultatmått |
Åtgärdsbeskrivning |
Tidsram |
---|---|---|
Biocompatiblity
Tidsram: 1 year
|
determine the subcutaneous connective tissue reactions to ProRoot MTA, Medcem MTA and Medcem Pure Portland Cement
|
1 year
|
Samarbetspartners och utredare
Sponsor
Studieavstämningsdatum
Studera stora datum
Studiestart (Faktisk)
Primärt slutförande (Faktisk)
Avslutad studie (Faktisk)
Studieregistreringsdatum
Först inskickad
Först inskickad som uppfyllde QC-kriterierna
Första postat (Faktisk)
Uppdateringar av studier
Senaste uppdatering publicerad (Faktisk)
Senaste inskickade uppdateringen som uppfyllde QC-kriterierna
Senast verifierad
Mer information
Termer relaterade till denna studie
Ytterligare relevanta MeSH-villkor
Andra studie-ID-nummer
- 13.02.2019 / 2019-02/04
Plan för individuella deltagardata (IPD)
Planerar du att dela individuella deltagardata (IPD)?
Läkemedels- och apparatinformation, studiedokument
Studerar en amerikansk FDA-reglerad läkemedelsprodukt
Denna information hämtades direkt från webbplatsen clinicaltrials.gov utan några ändringar. Om du har några önskemål om att ändra, ta bort eller uppdatera dina studieuppgifter, vänligen kontakta register@clinicaltrials.gov. Så snart en ändring har implementerats på clinicaltrials.gov, kommer denna att uppdateras automatiskt även på vår webbplats .
Kliniska prövningar på Mineraltrioxidaggregat
-
Beijing Friendship HospitalOkänd
-
Purdue UniversityOkändKronisk njursjukdom mineral- och benstörningFörenta staterna
-
University of MinnesotaIndiana UniversityAktiv, inte rekryterandeKroniska njursjukdomar | Fosfor- och kalciumstörningar | Kronisk njursjukdom mineral- och benstörningFörenta staterna
-
Great Ormond Street Hospital for Children NHS Foundation...Cukurova University; University of Kiel; Athens General Children's Hospital...Aktiv, inte rekryterandeKronisk njursjukdom mineral- och benstörningStorbritannien
-
Maimónides Biomedical Research Institute of CórdobaAvslutadKronisk njursjukdom mineral- och benstörningSpanien
-
Medical University of ViennaAvslutadSekundär hyperparatyreos | CKD-MBD - Chronic Kidney Disease Mineral and Bone Disorder | NjurersättningÖsterrike
-
Columbia UniversityNational Institute of Diabetes and Digestive and Kidney Diseases (NIDDK)AvslutadKronisk njursjukdom | Sekundär hyperparatyreos | Slutstadiet njursjukdom | Kronisk njursjukdom mineral- och benstörning | Renal osteodystrofiFörenta staterna
-
Thomas Nickolas, MD MSAvslutadVaskulär förkalkning | Kronisk njursjukdom mineral- och benstörning | Hyperparatyreos; Sekundär, Renal | Renal osteodystrofiFörenta staterna
-
Saint Petersburg State University, RussiaAvslutadSekundär hyperparatyreos | Dialys | Vaskulär förkalkning | Kronisk njursjukdom mineral- och benstörningRyska Federationen
-
Thomas Nickolas, MD MSAvslutadOsteoporos | Njurtransplantation; Komplikationer | Renal osteodystrofiFörenta staterna